304 304L Stainless Steel Sheet Plate Excellent Corrosion Resistance For Instrumentation

Product Categories

Jiangsu Junxuan International Trade Co., Ltd.

Contact Now

304 304L Stainless Steel Sheet Plate Excellent Corrosion Resistance For Instrumentation

Name: 304 304L Stainless Steel Sheet Plate Excellent Corrosion Resistance For Instrumentation
Brand: Vespolari Jiangsu
Price: 1 USD

Brand Name : Vespolari Jiangsu

Certification : ISO SGS ROHS

Place of Origin : Made in China

MOQ : 1Ton

Price : Negotiable

Payment Terms : TT L/C

Supply Ability : 10000000per month

Delivery Time : 7-15 Days

Packaging Details : standard waterproof package

Name : Stainless Steel Sheet Plate

Type : SS Tube

Length : 2000/2438/2500/3000/3048 Mm

Width : 1000/1219/1250/1500 Mm

Processing Service : Bending, Welding, Decoiling, Punching, Cutting

Surface : BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D

Contact Now

Excellent Corrosion Resistance 304 304L Stainless Steel Sheet Plate For Instrumentation

Item	stainless steel plate/sheet/coil
Grade	300/400/600 Series
Standard	JIS, AiSi, ASTM, GB, DIN, EN
Length	customized
Width	customized
Place of Origin	Shandong
Brand Name	Linxu
Type	plate/sheet/coil
Tolerance	±1%
Processing Service	Bending, Welding, Decoiling, Punching, Cutting
Surface Finish	2B
Delivery Time	10-15 days

Chemical Composition

Element	Type 430
Carbon	0.12 max.
Manganese	1.00 max.
Sulfur	0.030 max.
Phosphorus	0.040 max.
Silicon	0.75max.
Chromium	16.0 18.0
Nickel	0.60max.

Mechanical Properties

Type	Yield Strength 0.2% offset (KSI)	Tensile Strength (KSI)	% Elongation (2" Gauge length)	Hardness Rockwell
430 Ann	30 min.	65 min.	22 min	HRB 89

Physical Properties

Density (lb./ in^2) @ RT		0.278
Modulus of Elasticity in Tension (psi x 10^6)		29.0
Specific Heat (BTU/°F/lb.)	32 to 212 °F	0.11
Thermal Conductivity (BTU/hr/ft^2/ft)	212°F	13.8
	932°F	15.0
Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F)	32 to 212°F	5.7
	32 to 932°F	6.2
Electrical Resistivity (micro ohms - cm)	at 70°F	60.0
Melting Point Range (°F)		2600 - 2750
Oxidation Resistance - Continuous Service(°F)		1500

Processing

Type 430 should be annealed at 1450-1550F and furnace cooled at a rate of 50°F per hour to 1100°F and air cooled. If the annealing temperature does not exceed 1450°F (790°C), an air cool may be substituted for the furnace cool when annealing thin sections.

Forming

Type 430 is readily drawn and formed. Its drawing characteristics are similar to those of low-carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power.

Welding

Type 430 is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid brittle weld fractures during fabrication. When a weld filler is needed, AWS E/ER 308L and 430 are most often specified. Corrosion: This alloy is resistant to attack in a wide variety of corrosive media including nitric acid, and many organic acids.